Phase Structure and Electrochemical Performances of La0.63Gd0.2Mg0.17Ni3.0-xCo0.3Alx (x = 0.0, 0.1, 0.2, 0.3, 0.4) Alloys

N/A
N/A
Protected

Academic year: 2019

Share "Phase Structure and Electrochemical Performances of La0.63Gd0.2Mg0.17Ni3.0-xCo0.3Alx (x = 0.0, 0.1, 0.2, 0.3, 0.4) Alloys"

Copied!
11
0
0

Loading.... (view fulltext now)

Full text

Loading

Figure

Figure 1.  XRD patterns for La0.63Gd0.2Mg0.17Ni3.0-xCo0.3Alx (x = 0.0, 0.1, 0.2, 0.3, 0.4) alloys
Figure 3. Back scattered electron images for La0.63Gd0.2Mg0.17Ni3.0-xCo0.3Alx: (a) x = 0.0, (b) x = 0.1, (c) x = 0.2, (d) x = 0.3 and (e) x = 0.4 (A: CaCu5-type phase, B: Ce2Ni7-type (Gd2Co7-type) phase, C: CeNi-type phase)
Table 3. Summary of electrochemical performance for La0.63Gd0.2Mg0.17Ni3.0-xCo0.3Alx (x = 0.0, 0.1, 0.2, 0.3, 0.4) annealed alloy electrodes at 298 K
Figure 5. The cycling stability of La0.63Gd0.2Mg0.17Ni3.0-xCo0.3Alx (x = 0.0, 0.1, 0.2, 0.3, 0.4) annealed alloy electrodes at 298K
+3

References

Related documents

Generally, solder spheres for the use of outer joining of chip scale package (CSP) devices are required to have higher thermal fatigue properties. 1) However, using smaller

It is very difficult to get a high data completeness for this symmetry using the ’ scan mode only (‘Belok’ beamline limitation), even though we have run two different

In the external examinations NZQA uses a different approach to marking based on understanding (u), relational thinking (r) and abstract thinking (t).. They then allocate marks

Table 8 : Growth inhibition zone diameter (mm) developed when different bacterial strains were subjected to respective MICs of the ligand and Co(III) & Ni(II)

2 position Single Double 3 position Closed center Exhaust center Pressure center Double check Pilot type Manual override Main valve Pilot valve Coil rated voltage Porting