Overall, the leaf extracts were shown to have good corrosion inhibition efficiency of up to 96 % at the concentration of 1500 ppm from the anti- corrosion measurements
The corrosion rate ( CR ) and the values of inhibition efficiency (IE%) and degree of surface coverage ( θ ) obtained from gravimetric measurements of mild steel
The root extract of Angelica sinensis (AS) was examined as potential corrosion inhibitor of mild steel in 1 M sulphuric acid (H2SO4) media using weight loss, electrochemical
The present article is devoted to study ceftadizime (CZD) as corrosion inhibitor for mild steel in hydrochloric acid solution using electrochemical impedance spectroscopy
Weight loss data for corrosion of mild steel in 0.5M H 2 SO 4 solution in presence and absence of different concentrations of methanol leaf extract of Irvingia gabonensis..
The comparison of error results for the prediction of corrosion inhibition of mild steel by Sida Acuta’s leaf pastes in sulphuric acid medium using multiple regression
Abstract The corrosion inhibition of mild steel in 0.2M Sulphuric acid solution at room temperature by Alchornea Cordifolia leaf extract was studied using
The corrosion inhibition efficiency of the vasaka leaf extract for protecting mild steel in potable water (neutral aqueous medium) was studied by weight loss, Open circuit