THE DEVELOPMENT OF COPPER ALLOY METALLURGY IN THAILAND IN THE PRE-BUDDHIST PERIOD, WITH SPECIAL REFERENCE TO HIGH-TIN BRONZES

N/A
N/A
Protected

Academic year: 2020

Share "THE DEVELOPMENT OF COPPER ALLOY METALLURGY IN THAILAND IN THE PRE-BUDDHIST PERIOD, WITH SPECIAL REFERENCE TO HIGH-TIN BRONZES"

Copied!
92
0
0

Loading.... (view fulltext now)

Full text

(1)

THE DEVELOPMENT OF COPPER ALLOY METALLURGY IN THAILAND IN THE PRE-BUDDHIST PERIOD, WITH SPECIAL REFERENCE TO HIGH-TIN BRONZES

By

WARANGKHANA RAJP I TAK

B.Sc. (Chemistry), Chulalongkorn B.Sc. (Conservation), London

Thesis Submitted for the Degree of Doctor of Philosophy in the Faculty of Science of the University of London

Volume II

Department of Archaeological

Conservation and Materials Science University of London

(2)

P1.1 Beads from Ban Don Ta Phet

P1.2 Beads from Ban Don Ta Phet

j;;: :J'I

--. l,5.. =• - - -- I. - .

-'S

-

.-P1. 3 Beads from Ban Don Ta Phet

(3)

-U

-P1.4 Beads from Ban Don Ta Phet

P1.5 Finials from Ban Don Ta Phet

S

=__-I_

1

(4)

-

--P1.7 Finials from Ban Don Ta Phet

P1.8 Cockerel on a cage from Ban Don Ta Phet

(5)

32H

1

:s-:. ;;; irS

U

I

(

z

-P1.10 20% Sn quenched 750°C x448.8 Etched

' -' -r r I!'

9

/' /. 4t;

P1.11 20% Sn quenched 750°C x112.2 Etched

(6)

U

-'5 / -"I

/

ii,

-.'ct -

"I.--I

.5' -' ,c . - - - /

/-S

i4

P1 .13 20% Sn hot worked/quenched 750°C x56 .1 Etched

17

O

• \ \

\

\

j/\

$

'

\(

)

-

V . b.

P1.14 20% Sn hot worked/quenched 750°C x224.4 Etched

1-'.

I /

(7)

P1.16 20% Sn hot worked/quenched 750°C x1122 Etched

14

P1.17 20% Sn quenched 650°C x112.2 Etched

:..-•

Lpv'

.7,

(8)

.

a

I'(

(4i

w

P1.19 Std. 20% Sn quenched 550°C x56.1 Etched

P1.20 Std. 20% Sn quenched 550 0C x448.8 Etched

(9)

y,. - 5' ., V :. • ... 4 .. .! •.' \ç.., :. • '5 -:

.

1&

-S. '

i-•

:*

N.

S%4•

4.,

r:''

X ?

4;

jr

P1.22 Std. 20% Sn quenched 450°C x 224.4 Etched

- 'S

- -:; ;;;;; ;> - . -5' Sb

/ S.,

-P1.23 Std. 23% Sn quenched 750°C x112.2 Etched

(10)

m L. .. ' . ' ."

P1.25 Std. 23% Sn quenched 750°C x448.8 Etched

- -s s'•

"(a '-;• ', y ;. V.

-¶1 "' çYk

41

. ".-

i:

1

-

\?. .sl4i4

:b. ••• -

-'Cgr - b ••'

r*- ....

- •. - - '—• a

-p.. i(

:" .

-

-j;44

4;:

Ija

P1.26 Std. 23% Sn quenched 750°C x1122 Etched

-V

• :

'- '¼. - .• s:t. 4

.-• -c__ .4. I• .••

4 ,_•_ - .

-4 .-.. -

,---

- -

i-.-. ; --

% 'I',,

-*4

•--'

(11)

y(

4:

-d'-- . ...

.-T . .

s -.

k4' '

.A., --,' .-.

L. .. -. IL' •'' r 1

•_.:'..;_

.J

"(."

• -..

ps

q'

I.... '. ..- 3 -. S.'

.3.

. -.' '.-

' I .,...

;''

j 4'?

d A

P1.28 Std. 23% Sn quenched 650°C x 448.8 Etched • .

.c

P ... : .,

!?

liz'

- .,

.Td:.b_ ..3..' l4

4;•.•-•. ...* 4

P1.29 Std 23% Sn quenched 650°C x 112.2 Etched

-- —•

•-P1.30 Std. 23% Sn quenched 550°C x56.1 Etched

(12)

-/

I

,Y

P1.31 Std. 23% Sn quenched 550°C x 112.2 Etched

P1.32 Std. 23% Sn quenched 450°C x 56.1 Etched

(13)

,:

fr

.---d ,

• •2 - •'- •.. .4 •?I.

I - i:::;

'Z

b - • •. t

.- S -

I -- .:- - -- -• - .; ..

P1.34 Std. 24% Sn quenched 750°C x 56.1 Etched

xs. - 1c

' - - I

-I.

- - .- --• ••—.' -"S

-- •

- ::

Nt-:. b

'S ' f' • ' S •'...

s-': t . N '5SS

-k • ••••T

--- rn w

- S. -

:•-:. - - -- --. -

-5-

N5 •\S •-

-S..'

\ 155% - •• -

l," '

-.5••

5%•

.'--- 'S

P1.35 Std. 24% Sn quenched 750°C x224.4 Etched

('";J(

•.1;-J

ff'! Ht 1.

7 r:

T.-:

!u. t •

-/ 1

•Ii•

I --

i-r5-:.5j...I1

-'

•'.:

• 1 ;: h .,'_jL_1•

I,.'

i_-.- 1.1

I

I

• -

I

-

•-

v-:-•--_-- ill

:

-. —i- -- - I - -- - I

I J.

- I

-

-

-5----• —

).1

1 Ll

i'

,fi('i !J

•IScj.-i__I:_.:/

i .,_SI' . I. •f,

.

I.I.

I,! I I

II:

-

-5, -1.• ,

-;

•I

•'I! ii LI.

I

.54 III

!S..I

J

1

--•1 •

I

I-kEt'1i

(14)

/

Ii;''.

fr,_,'

,Y

; 4( 9pt ^t'I //fr4 p '

'I

/

/,,/4 ,//;.,

• ..:- 7

A:

N

' f i

//

.;-••- •.

P1.37 Std. 24% Sn quenched 650°C x224.4 Etched

- •'

-. - 4

I -

••j•"

3;

- - •A - - ••• --.'

-J!J -

Jr

:;;d:R:

h

-P1.38 Std. 24% Sn quenched 550°C x56.7 Etched

:.' /

".*

; .

(4-;';

1/

., .

••-'7g-

-j(7'

•• I - -,

(15)

4[:

////

•j1/1 !!

/%

:/ i/

/

-

Z----I

/

/

: / 1 i/' II

111/

1/1 ii

-

-

f -.-. - -. -- ---- - - .---

-;-.----a 14;'t

w ''::ij

? ;•'

--

: 4 .'

4

:--P1.40 Std. 24% Sn quenched 450°C x112.2 Etched

a ;.4)

/\\\.

t

<:

.

\"\L\

-"5'S1'4'

-):1 \'\\ \ p

-I'''

\

P1.41 Std. 24% Sn quenched 450°C xl122 Etched

P1.42 Std. 25% Sn qucuched 750°C x56.1 etched

(16)

-I

---- -- __

r - - _____

.;:

P1.43 Std. 25% Sn quenched 750°C x448.8 etched

-

---1

P1.44 Std. 25% Sn quenched 750°C x112.2 Etched

(17)

S

-,--liii !

k

I\ \

1 .

I /

•! /

1'

f/ .

\\\ ff

P

• /\"\

>\J I"\

/ \

/ .

I

\

'•':

P1.46 Srd. 25% Sn quenched 650°C x224.4 Etched

P1.47 Std. 25% Sn quenched 650°C x56.1 Etched

(18)

.5

-P1.49 Std. 25% Sn quenched 600 °C x112.2 Etched

P1.50 Std. 25% Sn quenched 600 °C x1122 Etched

-.-.

I?

________________________

.

- •.j. ' ..: S. 'I • - ________________________

•S_ \J $ i '

1.;,¼' .

• ..t-' S..S.S \. 'S

V / ,

. - _jxy,' V -. ;. -'. .SJ 4

- -!'

f.,r

---- 4.

-S. I. - .. . . . , ., -_._. c-. -. -. p. r . ..

r, -

-':

-'. )' •' — .

5 I /

' ... :-.- .-"r .;. . •- •- . ... . , ..

S :j - -.• .:-" ••. ' -i• •

.pt S - '.i I ..- - r -. '%,.

. , .. . •-: - H

(19)

-[:

I - , ...

jfr. .

4 J'•Q• od, (1

) , I 2*b L2 b TI0g ..' '

j, ,. 'r'. 8 '' •:- '?

d0,

16) J )I.

I

fo%t:

:?Pa .0 1

07Q. °

£1 °o..aog° 7) . -\_/ (J° j- °t cD V

'I 47 -. •

0.0 0 LI o O

(1 ° ç

___

I

k•

b

-.

1• /

\

s--,

IS 0

P1.52 Std. 25% Sn quenched 550°C x224.4 Etched

P1.53 Std. 25% Sn quenched 450°C x51.6 Etched

-. 4.,

4

,' t''1

(20)

--

--N --N .--N.

P1.55 Std. 26% Sn quenched 725°C x224.4 Etched

,

\\

\'\.\\\\\

'

,.•\\\ \% \'\ \"

\ \

\\\• ••\\.' \

P1.56 Std. 26% Sn quenched 725°C x1122 Etched

- I i-.- -

-

S-* \

\\. '

S

'• ' S

•t.J•...--

\ \ \

'\\

. \\

(21)

ç

p1.58 std. 26% Sn quenched 650°C x112.2 Etched

4.

P1.59 Std. 26% Sn quenched 650°C x224.4 Etched

- . . -

______

- • ..

/

'.'

.

.

(

- .?

;,fr$

I

$4

)34:

-

.

.

..

••• .

I ••

•-

•• . :-:.•

• .

..-\

(22)

-t...

P1.61 Std. 26% Sn quenched 550° x2244 Etched

P1.62 Std. 27% Sn quenched 725°C x56.1 Etched

(23)

;

-•

a

P1.64 Std. 27% Sn quenched 725°C x448.8 Etched

P1.65 Std. 27% Sn quenched 650°C x56.1 Etched

(24)

.:'

_____ L.

..-1,

jçj

-I,..

p.

P1.67 Std. 27% Sn quenched 550°C x56.1 Etched

- •• .- / /-

..-•

-1 . . .

. -: .°- :-;-

S t.

- -

A

i_miur.

T ;':.'. '..

P1.68 Std. 27% Sn quenched 550°C x224.4 Etched .

..

.pf'.•

;, •:-.,, ...

.j L, -.-..

#P...

- -,-: : •.

,

4v'

(25)

.__•I-,. I

p

.1

'1

Li

- - --., --.- S--, -_ -

-P1.70 Std. 28% Sn quenched 725°C x224.4 Etched

• r,...,. , .

-,

•'.

;r--.-• • • '4. ;

• '• A- ,(,','j-'- -

--_I4

• -.

' '- -,.

> ,'- •'S4

.; 'U

.,

-P1.71 Std. 28% Sn quenched 725°C x448.8 Etched

(26)

-' '

' •

--4' .

.-- -1 3

,- . , ,

i : ._.

q) , c1

_- , ' .'- j' -7?

V ';

- '

-y- -

.-.--4

• -•-••

P1.73 Std. 28% Sn quenched 600°C x224..4 Etched

• , y_ .-

•\_.

-

:-P1.74 Std. 28% Sn quenched 600°C x448.8 Etched

(27)

-q- ..

I.

iiL4

P1.76 Std. 30% Sn quenched 725°C x112.2 Etched

'Ip, •.

4...-P1.77 Std. 30% Sn quenched 725°C x224.4 Etched

• .- _c '" ':

k:k ;..-. s' '

- r '

• ..' Q

• . .

(28)

-y4.

4

Ii Cm

P1.79

1001

-

-I

1 Cm

P1.80

1001

(29)

P1.82

1001

x112.2

Unetched

- ,

_

-

-_

-x224.4

Etched

Etched

1

i . - / i.

7/'

P1.83

1001

x112.2

T••.

0..

(30)

-

----4A

'--'-

t

\\\

--

4:

-I--- -.

4Ih -- L k. -'f•

P1.85 1001 x448.8 Etched

L

-

- -. ;.

':':i,.

.

S

I- . 's': - - - p4

.

. •,ç 44 •t

F

.4

i & ...'. .

0

d,

'

\

,--ki.o&

-' Ic-,.I, ::

'

•i-.:

r k V. •:.

P1.86 1001 x112.2 Etched

• ' \

:

\\,,

\

,.. -'

-' -4 .'- --

r-La

f_

-.--_j-.

7r

•i

(31)

\V

.44

*P4

P1.88

N! /

b

- ..

) •,

.\

ç•-T

f

t'\

1001

x1254

Etched

JCm

P1.89

1004

(32)

-

'

. r

1• -. ':f'

:')'

[CmI

P1.91

1004

x224.4

Etched

P1.92

1004

x112.2

Etched

(33)

T

'

.'v

I

n_A.

'S• -

- ' •, .4

:--[lCmI

P1.94

1005

,;..

iYa;

;

• •. .. iI

I. 'I' 4

i

-t J .Ig a'

w:; ..•... '.:

..

S •.•' •. *

.:

-

.0

• •

e- - •'• .'

,, .

,J

P1.95

1005

x56.1

Unetched

'5.1

!

1*rP+c!c

:; '

..

'!!t;

& .. ç.AP).-5

c

* '

---

.

-,,

-P1.96

1005

x112.2

Etched

- ....

.

s_it.. . .

S..

S

&Th

S

_

•.r--

.1

-

:.

A

(34)

,%. .._ c.

7

.5

- . -"

S • S .•

S.

•#

-P1.97 1005 x224.4

-•: Y' •

:

Etched

:;

r.

;

;!

!t

!,. I • •

1..•.

-:

:

A .

--

I • *1r

-.

P1.98

1005

x56. 1

Etched

a

.,',

I.

r\yø

I

'5

p

S.

(35)

A

_z. -'

P1.102

1006

x448.8

Etched

P1.100

1006

(36)

-

-'\

P1.103

1006

x1122

Etched

P1.104

1007

(37)

P1.106 1007 x224.4 Unetched

p 1.107 1007 x112.2 Etched

(38)

.

P1.109 1007 x1122 1.tched

__ __

_ __

'i w i ____ _____ '

,tfylI'a

P1.110 1007 (long.section) x112.2 Etched

-

'-^

;

•a' '?I ;

.' •.' - *1 , %1%.r;

*. '

—' I•p ' f , . i

,

.:

SaU

(39)

I,

1

Criij

.

•1

i

'.4

•*4

P1.112

1007 (long.section) x1122 Etched

*;ir

%,

. ..ct.

,t,

I_I

1

ó

'

.g

'W S V9g

iL ',

L* ;

%F7JØfl

' .

..y'

l

41,.4j..s16,l!4r!:;

4 -

sJ

S

-

'I.

d d

P1.113

1007 (long.section) x112.2 Etched

(40)

• ___

r7.•'

-

--a

Is '

•.

;..

I

-4- '---'V

I-

•-L.

S

a - .

• .

S.

-P1.115

1008

x56.1

Unetched

P1.116 1008 x56..1 Etched

.•4

(41)

Cm]

P1.118

1009

P1.119

1009

(42)

P1.121 1009 x448.8 Unetched •

-•1 -.- r- -- -.

•_*_

r :Y-- •t

j"i--I

• - -_ --•

-

--P1.122 1009 x224.4 Etched

'

1

.

(43)

P1.124

1010

P1.125

1010

-.g

••'E '.:

A4 !TI

,

k

,

.1

4, ,.7,

I.

• --'..

. ,

I. •

r . I

.-.,.-'

.dp:1I

•L .'":r a

(44)

4

•-L 4LUJ'., ::

I

A

P1. 127

1010

x448. 8

Unetched

w.

a

. •4

I,

%,

-. 1'

P1.128

1010

x56.1

Etched

(45)

P1.130

1011

P1.131

1011

x224.4

Unetched

(46)

I.

P1.133

1012

P1. 134

1012

LlCj

-

..

vtlIr;

(47)

: :.

P1.136 1013 x56.1

'1;!

J.1

tinetched

P1.137 1013 x224.4 Unetched

T

(48)

11

C"

-I.

p

-P1.139 1013 x448.8 Etched

P1.140 1013 x1122 Etched

I'

•'"' A•

4

&

(49)

.

-'

-.

(lCrnI

P1.142 1014

P1.143 1014 x56..1 Unetched

cD

( ', I_L tr

L

(50)

.

- ________________

I'

P1.145 1014 x224.4

r

j,.. 4.

/)-:

• -'p•___.

1 • -' '

s

Etched

I

-w.,, .

• •I - ,-.

• •-.•-- •

P1.146 1014 x448.8 Etched

11Cm]

(51)

1016

x112.2

Etched

P1. 149

-j

-%

-4. .

..' #1

0'

P1.148

1016

p

y

Vi),

'

;,

'-x112.2

Unetched

L 1 Cml

(52)

,/4 Y

;-1

-P1.151 1017 x448.B Unetched

P1.152 1017 x448.8 Etched

- ' b- .

...---A-

- ..

S ,_-i . -.

-- _ - ; 'I. . •&.:' :

•-.1 •'.-4 -.-.

(53)

Cii

P1. 154

1018A

---

=---P1.155

1018A

x112.2

Etched

(54)

:a :

P1.157 1018A x448.8 Etched

-

* :

- "'c r_d.-. .. --'--i

-- -- .4

- - - /- ;

I'

-, ---. - •--- '. - I-

P1.158 1018A x250.8 Etched

(55)

P1.160 1018B x56.1 Etchcc

'

:E- . i .

.4._

jt

.'

_j'.zi_-\• .'..

P1.161 1018B

I;rt$P. . -

-:4

r- ..

x448.8 Etched

-. ur

L

:

A

____i.

L.

•--:

:z

..'

ø_ b

(56)

P1.164

1019

P1.165

1019

P1.163

1019

3..

[ (

(57)

r

1•

P1.166 1019 x56. Unetched

f

T-• -. -. 4

-_____

-p1.167 1019 x56.1 Etched F

• -

-p .-,-'r- •

• j .;:

•':

1.. ••-••

:jt

M;:

t*Zr

. -'.,. '.-'^."* .>- :' -- ',. 1.-

'?" 'i.ç

•,...-jc:' :< .

,

-k

'

-P1.168 1019 x448.8 Etched

-- g:---'--,

a U

(58)

;

- ..

.44 -

.1

.

11 Cml

ii

7

-

4 .

P1.169

1019

x1122

Etched

P1.170

1020A

(59)

itY i

,.y

I,

l•b

P1.172

1022

P1.173

1022

x56.1

Unetched

• )Q

S..

a

(60)

3..

,fr.l_ (

4 1

:

'-•

1022 x112.2 Etched

A

__

- C

.

S

. .. ,

P1.176 1022 x448.8 Etched

.

-b.,

ii-•

'a-•

- . 4

.

b

.

S..

. A

-. S-.

/

I

' b'

(61)

-, 4l L

1f .& 'I

4

.

(.

Jr r I

.-..

q

.: •1 , -.

.S.

•1.

1 Cml

P1.178

1023

P1.179

1023

x56.1

Unetched

(62)

L_L_L_1__LJ I4 4

•k .p

t_

1111_LI MM

P1.181 1023 x224.4 Etched

P1.182 1024

(63)

P1.184

1026

I

I

I-,

:

.

%4 \• •'.. '

J; •.

#

J.

I

L' .

i.Ll A

P1.185

1026

x56.1

Etched

;

/;\ kq

3.IlIty c4:.. ,

II•

'i4

I ' I ' S *

4 1.

•' /

..i!

..•t

I-fi

i I'

(64)

-5:.--.i

1-)' .

---1•

f

P1.187

1026

x448.8

Etched

i

p

.

/

:

:

P1.188

1026

x501.6

Etched

,

4;

411

''L'b.j

V

P1.189

1027B

(65)

a

P1.190 1027B x56.1 Unetched

p

4r4J

d

Ii.

4

rat.

• •

P1. 191

1027B x224.4 Etched

r

(66)

I

P1.193

1028

S.i

fF

I

I.. _.,. L. • r • .,.. 13

1.. .:

n

II

P1. 194

1028

4

-xi

P1.195

1028

x448.8

Unetched

(67)

P1.196 1028 x448.8 Unetched

P1.197 1029

d 4 F :.,... : ¶... -• .._-•. -, .1:.,

- I -. -.

_s,i____• .

* 7

£

•• , •_4_

. .,

L '._.*.

'..-':'• ;/.

.- _h.IP._.

-- -- '4P

I _.

,I

. I ,.• : • -

-.

. #'.\' • . 4

p

•. L.1 . r

':1:'- S

•--'• •• -,_. ,' & _..,

TCm

(68)

p1t

t

?

• - '-I..

:i;c•A

t"

;,*

e__

j

-.

P1. 199

1029

-

.-4

_ ..tI.. •

. --- - '

-.

4

-• -•.

4.. _a•.. -

••

--

Tr

1si

P1.200

1029

:

'

iç'.

•.••

,

. JI

) '

I

1

::j

:e'

'•'1

•1I.•

-

11.

-.

'.'Jjp

4•

- •; •-. • •

1

p •

-

-

Ø-..: ' -. . •'.•'• ,.',..

4

-•:

b •..

i.,

,-

.:-

•%S?

.•

e;¼

a_p.

••

. ••,,...

1

4$- % .

s"-s

•-.¼ •'. •

(69)

-'

-

4?.

:'.

.".• .;

•.; ,

% . L

:.

k.•;11;b .

iu')t

'%! .. -

'$

.

I...

P1.202

1029

x224.4

Etched

a

S

__

'lI•

4•

#p-løi'..

S

P1.203

1029

x448.8

Etched

1J

(70)

I

1Cm]

P1.205

1030

ci

-P1. 206

1030

x112.2

Unetched

C

C

4

,

44

I

x448.8

Unetched

(71)

?'

.

Jc

ft

-w .\

I -

q-4

hit i'

't-.d*

•I44jP

.

bj

-L1

Ci

-- .; --,,

bi.

P1.208 1031 x56.1 Etched

I.

P1.209 1031 x112.2 Unetched

(72)

P1.211

C

.J11IIIII

1032

x56.1

Unetched

-fi:

I

.

-P1.212

1032

x224.4

Etched

(73)

7

P1.214

1032

x501.6

Etched

•E' ) ..

-[Cry,

1

P1.215

1033

(74)

•__..'• •. . '' . :..:•:• : -• S S

•, S

•.S.

- :. •..

dP

-• %• S

S. •_•• S •

5_ S .••'..

i :

• • . S • 4p•. * ..

•5 •• ..

• . - . .

• • • - •

• •• -.

•-%

•. I •. • I

. •.•• •. •. S

_•_._

• .• - •. ..

•,• . #.. S

P1.217

1034

x56.1

Unetched

4

muh1MM

I I

•.•

I"

I

P1. 218

1034

x448.8

Unetched

W

-•

• S..

• •

11--•5

S •• ' V '.*r

; :

•. -

!'Tl..

••• ?

-1

• •d0

• b •

•*' ;

F a- . •. • , S.SlI• '

I

(75)

-

I

-

-'p

I4I

P1.220

1101

bf;*

"Y

-r ) /

P1.221

1101

x56.1

Unetched

(76)

-I.

P1.223

1101

x56.1

Etched

-IlCmI

P1.224

1102

(77)

P1.226

1102

x224.4

-

___

4à 1. -. jp

:•

i:;A !.

• . -..

_;_

-Unetched

.w. ..

t--S

., 2

T__

-. S

P1.227

1102

x224.4

Etched

:1

(78)

•l.• . —

4

(lCmI

P1.229

1103

LLJ

- —

P1.230

1104

• •1''

• • t .,.. S .. '. S.- - a •,•..P

r-

e S. •

S • •e ..s •

V

•51 , V

- •

. St

-I.

, -

-. •

r'

-'•

-, •

••

.-

.5..

•-,•1

--'-I.

• - • . . -

• •.

L4

(79)

$ 1

;.14i

'F.

:,:

•1-S ' -,

.,t.t

P1.232

1104

x224.4

Etched

IlCrnl

P1.233

1105

IlCmI

(80)

– '•

--M

'i.;jP:i

• 4

-f.

.... r.-; ,;

4.

ct' -.;. '.';_: ;'• 1

•ba

P1.235 1105 x224.4 Etched

,

!2

'r

:

.

a

yr :

1

.

.,

14

•s , .1

I

P1.236 1105 x448.8 Etched

'.• •_&

i

'r'J

ff.

"p

V ,

0

-c' ۥ '.4

t

,_•- ,.. k

__4sI•

(81)

-[1

Cml

P1.238

1106

P1.239

1106

x56.1

Unetched

(82)

P1.241 1106 x448.8 Etched

IlCmI

P1.242 1107

'

-. •

I

-4 •.• AI.P . ,

' .4:

- r

I •. ...

••••4

(83)

P1.245 1107 x448.8 Etched

P1.246 1108

tCm

:?ki

Ipi

p-o;

• ;

r•. ..

(84)

p •

-'

P1.247

1109

*4

IIb

A.

'

-,

-•

I'

4 4

P1.248

1109

x224.4

Etched

4V

J.

d

.

.%t4

(85)

P1.250 1109

-,.

LI

TiLrr

•;q4;.

'b,

I

r

./ /kki

1/

ii't

ti:t

x112.2 Etched

• I

I I

P1.251 1110

'ST

S •% c

a

•1

S

F'.

(86)

P1.253 1110 x56.1 Etched

•1

j

• •%_

P1.254 1110 x224 .4 Etched

LLJ

• .

- 1 - T 11 :uiuu..

-:

(87)

P1.256

1111

x56.1

Unetched

P1. 257

1111

P1.258

1111

x56.1

Etched

S

(88)

P1. 259

1111

x1122

Etched

o

IlCrnI

- -,

P1.260

1112

(89)

[Cm

.. t

...

.p_IIp-•

I

S

C

A

P1.262

1112

x448.8

Etched

P1.263

1113

(90)

P1.266 1115 x56.1 Etched

LLci

P1.265 1115 x112.2 Unetched

(91)

S.

a

I'

I

a

.'•..' .•

w.

*' .;

1!o ?

.

::.f.-.

.d''#Pi'•&%

.,te_

S." ,b;•;

J._:.

"iC',,..'*

4''

•$?P$

•':.

d:4PI,^

cc

. ".:.

.*

•:k;

P1.268 1116 x56.1 Unetched

P1.269 1116 x448.8

Unetched

-'

• I

p.

I ' A)

1;

(92)

Ia..

Zi

:1

P1.271 1116 x56.1 Etched

P1.272 1116 x112.2 Etched

P1.273 1116 x448.8 Etched

References

Related documents

To accomplish our objectives, we (a) obtained copies of the associated Voucher Invoice System (VIP) reports containing cost infonnation submitted by the four subcontractors;

With the aim of controlling the aircraft along lateral, vertical and longitudinal axis , and in order to respect NFZ and waypoints constraints along the optimum 4DT,

recommendations related to core competencies for drug court prosecutors which include specific roles and tasks to be undertaken by the prosecutor. Recommendation: The role

In this research, the physicochemical, textural, vola- tile, and sensory profiles of traditional Sepet cheese, and changes in physicochemical and volatile composi- tion

assumptions, formulas, etc. so that a reviewer could replicate the calculations based on the data provided. All assumptions and estimates must be clearly identified. As noted in

As regards the creation of value, it was seen, that if the company has high costs resulting from the large investment carried out in acquiring and implementing the technology

For this study an existing rural distribution network (Bulhoek/Middleburg 22kV) in South Africa with small scale hydro generation is analysed to determine the effect of

Questions about whether wholesale markets will bring forth adequate investments in generating capacity arises naturally from the unusual characteristics of electricity supply