This may be the author’s version of a work that was submitted/accepted for publication in the following source:
Kalaoglu-Altan, Ozlem, Verbraeken, Bart, Lava, Kathleen, Gevrek, Tugce Nihal, Sanyal, Rana, Dargaville, Tim, De Clerck, Karen, Hoogenboom, Richard, & Sanyal, Amitav
(2016)
Multireactive poly(2-oxazoline) nanofibers through electrospinning with crosslinking on the fly.
ACS Macro Letters, 5(6), pp. 676-681.
This file was downloaded from: https://eprints.qut.edu.au/97879/
c
Consult author(s) regarding copyright matters
This work is covered by copyright. Unless the document is being made available under a Creative Commons Licence, you must assume that re-use is limited to personal use and that permission from the copyright owner must be obtained for all other uses. If the docu-ment is available under a Creative Commons License (or other specified license) then refer to the Licence for details of permitted re-use. It is a condition of access that users recog-nise and abide by the legal requirements associated with these rights. If you believe that this work infringes copyright please provide details by email to [email protected]
Notice: Please note that this document may not be the Version of Record
(i.e. published version) of the work. Author manuscript versions (as Sub-mitted for peer review or as Accepted for publication after peer review) can be identified by an absence of publisher branding and/or typeset appear-ance. If there is any doubt, please refer to the published source.
Multireactive Poly(2-oxazoline) Nanofibers through
Electro-spinning with Crosslinking on the Fly
Ozlem I. Kalaoglu-Altan,a Bart Verbraeken,c Kathleen Lava,c Tugce Nihal Gevrek,a Rana Sanyal,
a,b Tim Dargaville,d Karen De Clerck,e Richard Hoogenboomc* and Amitav Sanyal a,b* aBogazici University, Department of Chemistry, Bebek, 34342, Istanbul, Turkey.
bBogazici University, Center for Life Sciences and Technologies, Istanbul, Turkey.
cSupramolecular Chemistry Group, Department of Organic and Macromolecular Chemistry, Ghent University,
Krijgslaan 281 S4, Ghent, Belgium.
dQueensland University of Technology, 2 George Street, 4001, Queensland, Australia.
eDepartment of Textiles, Ghent University, Technologiepark 907, B-9052 Zwijnaarde, Ghent, Belgium.
ABSTRACT: Crosslinked hydrophilic poly(2-oxazoline)-based nanofibers amenable to facile
multi-functionalization are fabricated using alkene-containing poly(2-alkyl-2-oxazoline)s (PAOx) via in situ photo-initiated radical thiol-ene conjugation during electrospinning. The resulting crosslinked nanofibers are demonstrated to be multi-functionalizable using different chemistries as they contain two functional handles, being the alkene moieties from the parent copolymer and the residual thiol groups from the tetra-thiol based crosslinker. While the thiol groups in these nanofibers could be passivated or conjugated to install functional molecules through thiol-maleimide conjugation, the alkene groups could sequentially be modified with thiol-containing molecules using photo-initiated radical thiol-ene reactions. Utilization of the photochemically induced conjugation of thiol-bearing molecules to the alkene groups on the nanofibers is used to obtain functionalization in a spatially controlled manner.
Polymeric nanofibers have emerged as attractive building blocks for various functional materials that find applications in several areas of materials and biomedical sciences.1-3 Unique properties of nanofibers such as very high surface to volume ratio, high porosity and structural similarity to the biological extracellular matrix render them with attractive attributes for various applications. Fabrication of polymeric nanofibers is readily achieved using electrospinning, a simple and robust technique.4,5 A high electric field applied to the droplet of a polymer solution or melt extruded from the tip of a spinneret results in ejection of a charged jet to the collector,
which is the counter electrode. Solvent evaporation and whipping of the jet during the flight leaves a non-woven nanofibrous mesh on the collector.
While the nanofibrous morphology provides advantages like increased surface area, it is often necessary to append functional moieties onto these nanofibers to tailor them for particular applications. This necessitates development of facile methodologies for their efficient functionalization under mild conditions. Prior attempts at creating surface active nanofibers from non-reactive polymers involve plasma or wet chemical treatments to install carboxylic acids and alcohols.6,7 These treatments are harsh, possess limited efficiency and can compromise the mechanical stability of the nanofibers. An attractive alternative is electrospinning of nanofibers from polymers possessing reactive handles. Advances in ‘click’ reaction based post-polymerization functionalization over the past several years have made such conjugations routine for accessing functional materials.8-10 To date, click reactions such as copper catalyzed Huisgen
azide-alkyne cycloaddition,11 strain-promoted azide-alkyne cycloaddition,12,13 radical thiol-ene,14 Michael additions,15 and the Diels-Alder cycloaddition reactions16 have been employed for nanofiber modifications.17 Until recently, multifunctional nanofibers remained largely unexplored beside the recent elegant example of ‘tri-functionalizable’ nanofibers by the Becker group,18 where they co-electrospun two different caprolactone-based copolymers containing three different reactive handles, and functionalized them with various dyes and peptides.
While noteworthy advancements have been made in the area of functionalizable synthetic nanofibers, most studies have focused on fibers obtained using hydrophobic polymers. Approaches towards fabrication of hydrophilic electrospun fibers are quite limited since as spun fibers will dissolve in aqueous media unless stabilized through physical or chemical crosslinking. Most of the studies in this direction have focused on poly(vinyl alcohol) which has been chemically crosslinked using treatment with glutaraldehyde.19 More recently, Burdick and coworkers reported the electrospinning of norbornene-functionalized hyaluronic acid together with a dithiol and subsequent post-electrospinning UV-crosslinking.20 The resulting crosslinked nanofibers could be further modified with thiols through thiol-ene chemistry. Given the significance of hydrophilic nanofibrous substrates in biological applications such as sensing or as scaffold materials, facile access to such fibers that can be functionalized in a modular fashion is quite important. Extension of various crosslinking methodologies to other classes of polymers
than those mentioned above is also a must to expand the utility of these nanofibers in various biomedical areas.
In recent years, poly(2-alkyl-2-oxazoline)s (PAOx), tertiary amide analogues of polypeptides, obtained using cationic ring-opening polymerization of the 2-oxazoline monomers have emerged as an important class of polymers suitable for various biomedical applications due to their resemblance to poly(ethylene glycol)s with regard to biocompatibility and ‘stealth’ behavior.21-24 Utilization of ‘clickable’ functional group bearing initiators and monomers provides well-defined copolymers that can undergo both side chain and end group functionalization.25-28 Among the various available ‘click’ type transformations, the radical thiol-ene reaction has been extensively employed due to its mild and metal catalyst-free conditions.29,30 Thiol-ene chemistry in combination with PAOx was first reported by Schlaad and coworkers,31 after which it has
become a popular tool as the ene-group can be introduced in the monomer and does not interfere with the living cationic ring-opening polymerization.32-39Among the limited number of reports on PAOx based nanofibers, electrospinning of poly(2-ethyl-2-oxazoline) (PEtOx) was reported by Iruin and coworkers to obtain non-crosslinked nanofibers.40 Also, composite nanofibers were obtained by electrospinning an aqueous solution of PEtOx and Co(CH3COO)2.4H2O which were
then calcined to yield ceramic nanofibers.41 Recently, Groll and coworkers reported the melt electrospinning of PEtOx resulting in fibers with diameters between 8 to 138 µm.42
Here we report, for the first time, the fabrication of multifunctional hydrophilic nanofibers using in-situ UV-crosslinking of poly(2-oxazoline) copolymers with a thiol-containing crosslinker during electrospinning. The alkene moiety of poly(2-ethyl-2-oxazoline-co-2-(but-3-enyl)-2-oxazoline) (P(EtOx-co-ButEnOx)) was used for crosslinking via the photochemical radical thiol-ene reaction in the presence of a tetra-thiol and a photoinitiator (Figure 1). After their fabrication, multi-functionalization of these crosslinked fibers in a modular fashion by modification of the remaining thiol and ene groups from the crosslinker and the polymer, respectively, was probed through attachment of two different fluorescent dyes via the radical thiol-ene and Michael-type nucleophilic thiol-ene conjugation reactions using the residual alkene and thiol groups, respectively. Furthermore, spatially controlled functionalization of crosslinked nanofibers was also demonstrated via radical ene reaction in the presence of a thiol-appended fluorescent dye and photoinitiator upon irradiation through a photomask.
Figure 1. Schematic illustration of fabrication of PAOx-based crosslinked nanofibers using in situ UV-crosslinking during electrospinning and their subsequent multifunctionalization.
Nanofibers were prepared by solution electrospinning of the alkene-side chain containing polymer P(EtOx-co-ButEnOx) in the presence of pentaerythritol tetrakis(3-mercaptopropionate) as the thiol containing crosslinker and 2,2-dimethoxy-2-phenylacetophenone (DMPA) as the photo initiator under irradiation with an UV lamp (365 nm) during electrospinning. It was envisioned that the alkene functionalized PAOx will undergo crosslinking via the radical thiol-ene reaction as the fibers are deposited on the collector. Following optimization experiments, a 52 wt% solution of the polymer in DMF:THF (1:1) was found to produce bead-free fibers with an average diameter of 542 nm ± 231 nm through electrospinning of the relatively low molar mass PAOx with a number average molar mass of 18,0 kg/mol and a dispersity of 1.14 (Figure 2a). Nanofibers were produced using varying stoichiometry of alkene:tetrathiol:DMPA, and thereafter subjected to rinsing with water to examine their stability due to crosslinking. When electrospun fibers obtained using molar ratios of 30:5:1, 30:10:1, 30:10:4 (alkene:tetrathiol:DMPA) were used, the fibers were not stable in aqueous environments and mostly underwent dissolution. It was only upon addition of a higher amount of the tetrathiol crosslinker (30:20:4) that robust nanofibers were obtained that were stable in water, and maintained their fibrous morphology, for prolonged periods of time (Figure 2b). Requirement of a higher amount of the tetra-thiol based
crosslinker is not unexpected since this low molar mass component does not possess entanglements like the polymer chains and tends to partially evaporate after ejection from the nozzle during electrospinning. Interestingly, an alternative approach where similar combination of polymer, tetrathiol and DMPA was electrospun to yield fibers, followed by UV-irradiation after electrospinning did not yield fibers resistant to dissolution, perhaps due to inefficient crosslinking resulting from low chain mobility in the dry nanofiber. Stable non-dissolving nanofibers were not achievable in the absence of either the tetrathiol or UV-irradiation. Furthermore, the presence of the ester carbonyl groups belonging to the tetrathiol in the crosslinked nanofibers was evidenced by FT-IR spectroscopy supporting that crosslinking takes place via chemical conjugation by thiol-ene reaction (Figure S-1).
Apart from tunable hydrophilicity, the PAOx are also known to exhibit thermoresponsive behavior dependent on their side chain functionality and composition.43 The
P(EtOx-co-ButEnOx) copolymer study here was found to exhibit a lower critical solution temperature and a cloud point temperature of 75 oC in a 5 mg/mL aqueous solution. We examined whether the surfaces coated with these nanofibers also show thermoresponsive wetting behavior. The contact angle of a droplet of water on these surfaces was 70o at 25 oC while a significant increase to 90o was observed upon heating to 70 oC (Figure 2c). When the surfaces were cooled back to room temperature, the contact angle returned to 70o. These fibers could reversibly be cycled between
these two wettability states by simple heating and cooling treatments (Figure S-2).
Figure 2. SEM images of nanofibers a) dry b) after immersion in water for 48h and c) thermoresponsive behavior of nanofibers probed with change in water contact angle with temperature.
A closer examination of the functionality of the polymer and crosslinker (Figure 3) suggests it is possible to obtain an insoluble network long before complete consumption of the alkene and thiol groups. The hypothetical availability of these two functional handles should allow attachment of different molecules through two different reactions. The residual alkenes can be conjugated with thiol containing molecules using the radical thiol-ene reaction (Route A, Figure 3). Alternatively, nucleophilic thiol-maleimide conjugation can be used to attach desired molecules using the residual thiol groups arising from the crosslinker (Route B, Figure 3). Furthermore, these fibers can be sequentially treated with maleimide & thiol containing molecules to accomplish multi-functionalization (Route C, Figure 3).
Figure 3. Functionalization of P(EtOx-co-ButEnOx) nanofibers.
First, functionalization of residual alkene groups was investigated. Nanofibers were exposed to a thiol-containing fluorescent dye, namely, BODIPY-SH, in the presence of DMPA under UV irradiation. After rinsing of the fibers with THF to remove residual unbound dye, fibers were examined via fluorescence microscopy. Bright green fluorescence of the dye functionalized fibers suggested efficient dye conjugation. Not surprisingly, as a control experiment, when fibers were
N N O O N N OH O O O S O O O SH O O O O HS N N O O N N OH O O S N O O RHODAMINE BODIPY SH DMPA, UV (365 nm) N N O O N N OH O O O S O O O SH O O O O HS N N O N N OH O O S S BODIPY O S BODIPY N N O O N N OH O O O S O O O S O O O O S N N O N N OH O O S S BODIPY O SBODIPY N O O RHODAMINE N O O RHODAMINE ROUTE A ROUTE B ROUTE C DMPA, UV (365 nm) BODIPY SH N N O O N N OH O O O S O O O S O O O O S N N O O N N OH O O S N N O O O O RHODAMINE RHODAMINE x y z t x y z t x y z t x y z t x y t z x y t z x y t z x y t z
treated with the dye alone without any UV-exposure, a faint green fluorescence was clearly observable on the fibers indicating attachment of the thiol-containing dye, albeit in low efficiency (Figure S-3). It was likely that this occurs due to the presence of residual thiol groups on the fibers that form disulfide linkages with the thiol containing fluorescent dye. Indeed, the presence of residual thiol functional was confirmed using Ellman’s reagent based on the appearance of a distinct absorbance at 412 nm belonging to the pyridothione fragment that is released into solution after reaction with the fibers. (Figure S-4). To probe this further, we treated the as spun nanofibers with N-ethylmaleimide to passivate the thiol groups before treatment with BODIPY-SH in the absence of UV irradiation. As anticipated, negligible fluorescence was observed for these fibers that only possessed the alkene groups (Figure 4a inset). In contrast, nanofibers passivated with N-ethylmaleimide, when irradiated with UV in the presence of BODIPY-SH and DMPA, showed strong green fluorescence, indicating efficient functionalization (Figure 4a). Notably, three individual batches of crosslinked nanofibers obtained under identical conditions contained similar amounts of residual thiols (4.63 ± 0.45 x 10-5 mmol/mg) upon Ellman analysis, as well as exhibited similar fluorescence upon functionalization with dyes.
Figure 4. Fluorescence microscopy images of a) BODIPY-SH treated nanofibers via thiol-ene reaction after ethylmaleimide conjugation (inset: control without UV exposure after N-ethylmaleimide) b) rhodamine-maleimide treated nanofibers (inset: after N-ethylmaleimide conjugation).
Thiol groups on the crosslinked nanofibers were examined towards functionalization via Michael-type reaction using a maleimide-functionalized rhodamine dye. After incubation for 4 h, unbound dye was washed off with excess methanol. The red fluorescence of the nanofibers observed using fluorescence microscopy confirmed successful conjugation of the dye (Figure 4b). As a control, fibers were first treated with N-ethylmaleimide in order to passivate the free thiols and then treated with the maleimide-appended rhodamine dye. After incubation for 4 h
fiber coated surfaces were washed with methanol. Inspection of the fluorescence images shows relatively weak signal when compared to the non-passivated fibers (Figure 4b inset).
To demonstrate spatial control of the nanofiber functionalization, an exclusive advantage of using the photochemically promoted radical thiol-ene based conjugation strategy, attachment of BODIPY-SH under UV exposure through a photomask was probed. For this purpose, nanofibers were electrospun on silicon wafers and treated with N-ethylmaleimide to passivate the residual thiol groups. Thereafter, the fibers were imbibed with a mixture of BODIPY-SH and DMPA in THF and a photomask was placed on the fiber coated surface. After exposure to UV irradiation, the photomask was peeled off, unbound dye was rinsed off with THF and the nanofiber coated surface was dried under nitrogen. Successful patterning was clearly observed with fluorescence microscopy (Figure 5).
Figure 5. patterning of P(EtOx-co-ButEnOx) nanofibers with BODIPY-SH. Photo-patterning of P(EtOx-co-ButEnOx) nanofibers with BODIPY-SH.
The dual-functionalization capacity of these nanofibers sequential conjugation of maleimide-rhodamine using thiol-maleimide coupling, followed by attachment of BODIPY-SH under photochemical radical thiol-ene conditions was performed. After attachment of the first dye, unreacted dye was removed by thoroughly rinsing the fibers with methanol. Analysis of these fibers using fluorescence microscopy demonstrated that both dyes were efficiently attached onto the nanofibers, unambiguously demonstrating their multi-reactive nature (Figure 6).
Figure 6. a) Step-wise Dual functionalization. Fluorescence images of sequentially functionalized nanofibers with b) rhodamine maleimide and c) BODIPY-SH and d) dual-functionalized (merged image).
In conclusion, fabrication of crosslinked hydrophilic nanofibers that are amenable to facile multi-functionalization is accomplished in a single step using an in situ thiol-ene crosslinking during electrospinning. Hydrophilic polymers containing pendant alkene moieties are crosslinked using a tetra-thiol to provide robust electrospun fibers. These nanofibers readily undergo dual-functionalization under mild conditions using the nucleophilic thiol-maleimide and the photochemical radical thiol-ene conjugations. It can be envisioned that facile fabrication and functionalization of these PAOx-based materials, an upcoming surrogate of the widely utilized PEG-based biomaterials, will make these nanofibers attractive candidates for many applications.
ASSOCIATED CONTENT
The supporting information is available free of charge via the Internet at http://pubs.acs.org.”
AUTHOR INFORMATION Corresponding Authors
*E-mail: [email protected] *E-mail: [email protected] ACKNOWLEDGMENT
R.S. acknowledges funding from Ministry of Development of Turkey for grant No. 2009K120520. B.V. and R.H. acknowledge financial support from IWT and FWO Flanders.
REFERENCES
1. Teo, W. and Ramakrishna, S. Nanotechnology 2006, 17 (14), 89-106.
2. Wu, J.; Wang, N.; Zhao, Y.; Jiang, L. J. Mater. Chem. A 2013, 1 (25), 7290-7305. 3. Bhardwaj, N. and Kundu, S.C. Biotechnol. Adv. 2010, 28 (3), 325-347.
4. Greiner, A. and Wendorff, J.H. Angew. Chem. Int. Ed. 2007, 46 (30), 5670-5703.
5. Huang, Z.M.; Zhang, Y.Z.; Kotaki, M.; Ramakrishna, S. Compos. Sci. Technol. 2003, 63 (15), 2223-2253.
6. Yang, F.; Wolke, J.G.C.; Jansen, J.A. Chem. Eng. J. 2008, 137 (1), 154-161.
7. Chen, F.; Lee, C.N.; Teoh, S.H. Mater. Sci. Eng. C. Mater. Biol. Appl. 2007, 27 (2), 325-332. 8. Lutz, J-F. Angew. Chem. Int. Ed. 2008, 47 (12), 2182-2184.
9. Becer, C. R.; Hoogenboom, R.; Schubert, U.S. Angew. Chem. Int. Ed. 2009, 48 (27), 4900-4908.
10. Durmaz, H.; Sanyal, A.; Hizal, G.; Tunca, U. Polym. Chem. 2012, 3, 825-835. 11. Shi, Q.; Chen, X.; Lu, T.; Jing, X. Biomaterials, 2008, 29 (8), 1118–1126.
12. Zheng, J.; Liu, K.; Reneker, D.H.; Becker, M.L. J. Am. Chem. Soc. 2012, 134 (41), 17274-17277.
13. Smith Callahan, L.A.; Xie, S.; Barker, I.A.; Zheng, J.; Reneker, D.H.; Dove, A.P.; Becker, M. L. Biomaterials 2013, 34 (36), 9089-9095.
14. Lin, F.; Yu, J.; Tang, W.; Zheng, J.; Xie, S.; Becker, M.L. Macromolecules 2013, 46 (24), 9515-9525.
15. Yang, H.; Zhang, Q.; Lin, B.; Fu, G.; Zhang, X.; Guo, L. J. Polym. Sci., Part A: Polym. Chem. 2012, 50 (20), 4182-4190.
16. Kalaoglu-Altan, O.I.; Sanyal, R.; Sanyal, A. Biomacromolecules 2015, 16 (5), 1590-1597. 17. Kalaoglu-Altan, O.I.; Sanyal, R.; Sanyal, A. Polym. Chem. 2015, 6, 3372-3381.
18. Zheng, J.; Hua, G.; Lin, F.; Yu, J.; Wade, M.B.; Reneker, D.H.; Becker, M.L. ACS Macro Letters 2015, 4 (2), 207-213.
19. Tang, C.; Saquing, C.D.; Morton, S.W.; Glatz, B.N.; Kelly, R.M.; Khan, S.A. ACS Appl. Mater. Interfaces 2014, 6 (15), 11899-11906.
20. Wade, R.J.; Bassin, E.J.; Gramlich, W.M.; Burdick, J.A. Adv. Mater. 2015, 27 (8), 1356-1362.
21. Sedlacek, O.; Monnery, B.D.; Filippov, S.K.; Hoogenboom, R.; Hruby, M. Macromol. Rapid Commun. 2012, 33 (19), 1648-1662.
22. Adams N. and Schubert, U. Adv. Drug Deliver. Rev. 2007, 59 (15), 1504-1520.
23. Luxenhofer, R.; Han, Y.; Schulz, A.; Tong, J.; He, Z.; Kabanov, A.V.; Jordan, R. Macromol. Rapid Comm. 2012, 33 (19), 1613-1631.
24. Barz, M.; Luxenhofer, R.; Zentel, R.; Vicent, M.J. Polym. Chem. 2011, 2, 1900-1918. 25. Hoogenboom, R. Angew. Chem. Int. Ed. 2009, 48 (43), 7978-7994.
26. Rossegger, E.; Schenk, V.; Wiesbrock, F. Polymers, 2013, 5 (3), 956-1011. 27. Le Fer, G.; Amiel, C.; Volet, G. Eur. Polym. J. 2015, 71, 523-533.
28. Lava, K.; Verbraeken, B.; Hoogenboom, R. Eur. Polym. J. 2015, 65, 98-111. 29. Hoyle, C.H. and Bowman, C.N. Angew. Chem. Int. Ed. 2010, 49 (9), 1540-1573. 30. Lowe, A.B. Polym. Chem. 2014, 5, 4820-4870.
31. Gress, A.; Völkel, A.; Schlaad, H. Macromolecules 2007, 40, 7928-7933. 32. Diehl, C. and Schlaad, H. Macromol. Biosci. 2009, 9 (2), 157-161. 33. Cortez, M.A. and Grayson, S.M. Macromolecules 2010, 43, 4081-4090.
34. Kempe, K.; Hoogenboom, R.; Schubert, U.S. Macromol. Rapid Commun. 2011, 32 (18), 1484-1489.
35. Schenk, V.; Ellmaier, L.; Rossegger, E.; Edler, M.; Griesser, T.; Weidinger, G.; Wiesbrock, F. Macromol. Rapid Commun. 2012, 33 (5), 396-400.
36. Tauhardt, L.; Pretzel, D.; Kempe, K.; Gottschaldt, M.; Pohlers, D.; Schubert, U.S. Polym. Chem. 2014, 5, 5751-5764.
37. Schenk, V.; Rossegger, E.; Ebner, C.; Banger, F.; Reichmann, K.; Hoffmann, B.; Höpfner, M.; Wiesbrock. F. Polymers 2014, 6 (2), 264-279.
38. Dargaville, T.R.; Forster, R.; Farrugia, B.L.; Kempe, K.; Voorhaar, L.; Schubert, U.S.; Hoogenboom, R. Macromol. Rapid Commun. 2012, 33 (19), 1695-1700.
39. Farrugia, B.L.; Kempe, K.; Schubert, U.S.; Hoogenboom, R.; Dargaville, T.R. Biomacromolecules 2013, 14, 2724-2732.
40. Buruaga, L.; Gonzalez, A.; Iruin, J.J. J. Mater. Sci. 2009, 44 (12), 3186-3191 41. George, G. and Anandhan, S. J. Sol-Gel. Sci. Technol. 2013, 67 (12), 256-266.
42. Hochleitner, G.; Hümmer, J.F.; Luxenhofer, R.; Groll, J. Polymer 2014, 55 (20), 5017-5023.
43. Kempe, K.; Neuwirth, T.; Czaplewska, J.; Gottschaldt, M.; Hoogenboom, R.; Schubert, U.S. Polym. Chem. 2011, 2, 1737-1743.