Resin Composite

A Novel Antibacterial Dental Resin Composite

A Novel Antibacterial Dental Resin Composite

... Figure 3 shows the effect of human saliva on the S. mutans viability after culturing with the modified com- posite. No statistically significant differences in the S. mutans viability were found between the composites ...

6

In-vitro Comparison of the Impact of Four Types of Resin  Composite on the Repaired Bond Strength and Surface  Roughness After Sandblasting

In-vitro Comparison of the Impact of Four Types of Resin Composite on the Repaired Bond Strength and Surface Roughness After Sandblasting

... Silorane-base resin composite had higher sur- face roughness after sandblasting compared with Micro-hybrid and Nano-hybrid resin ...p90 composite. Higher bond strength of this resin ...

8

Assessment of microleakage of class V restored by resin composite and resin-modified glass ionomer and pit and fissure resin-based sealants following Er:YAG laser conditioning and acid etching: in vitro study

Assessment of microleakage of class V restored by resin composite and resin-modified glass ionomer and pit and fissure resin-based sealants following Er:YAG laser conditioning and acid etching: in vitro study

... the resin composite, the resin-modified GIs, and the fissure sealant placement, may be an alternative enamel and dentin etching method to acid etching; however, further research with larger samples ...

10

Influence of ozonated water application on resin composite adhesive resistance

Influence of ozonated water application on resin composite adhesive resistance

... system and composite resin. EDTA solution has dentin collagen fibers chelating effect, which can increase the bond strength with the adhesive system, especially in the autoconditions, where the ...

5

Factors influencing repair of dental restorations with resin composite

Factors influencing repair of dental restorations with resin composite

... Fracture of tooth tissue adjacent to a restoration may occur for various reasons, including parafunctional activ- ity or trauma, or be subsequent to the damaging effects of polymerization stresses in resin ...

7

Bond strength of a universal bonding agent and other contemporary dental adhesives applied on enamel, dentin, composite, and porcelain

Bond strength of a universal bonding agent and other contemporary dental adhesives applied on enamel, dentin, composite, and porcelain

... dentin, resin composite, and ...and composite) or shear/SBS test (enamel and porcelain). In composite and porcelain, negative (no treatment) and positive (silane + SB) control groups were ...

10

Flowable Resin Composites: A Systematic Review and Clinical Considerations

Click here to download PDF version of the article !

... using resin- composite materials ...flowable composite resins is low strength compared to conventional composite resin, attributed to a low amount of filler, necessary for achieving low ...

7

Experimental and Numerical Study of Impact Energy Absorption of Safety Important Honeycomb Core Sandwich Structure

Experimental and Numerical Study of Impact Energy Absorption of Safety Important Honeycomb Core Sandwich Structure

... sandwich composite made from woven glass fiber and polyvinylester resin composite facesheets and polypropylene honeycomb core that can be used for safety important ...

6

An in Vitro Comparison of Bonding Effectiveness of Different Adhesive Strategies on Erbium:Yttrium Alluminum Garnet Laser Irradiated Dentin

An in Vitro Comparison of Bonding Effectiveness of Different Adhesive Strategies on Erbium:Yttrium Alluminum Garnet Laser Irradiated Dentin

... light-curing resin com- posite was scrubbed for 20s using the provided brush that has been specially modified to make it smaller so that it can enter the hole of the silicon ...the resin composite ...

11

In-vitro Shear Bond Strength of a Nano-composite Resin in Comparison with Microfilled and Microhybrid Composite Resins

In-vitro Shear Bond Strength of a Nano-composite Resin in Comparison with Microfilled and Microhybrid Composite Resins

... Nanotechnology has a significant contribution in resin composite research. Due to the reduced dimension of particle size and a variable size distribution, an increased filler load can be achieved with the ...

6

Comparative evaluation of fluoride release and shear bond strength of a polyacid - modified composite resin, a resin modified glass ionomer cement and a conventional composite resin: An Invitro study

Comparative evaluation of fluoride release and shear bond strength of a polyacid - modified composite resin, a resin modified glass ionomer cement and a conventional composite resin: An Invitro study

... modified resin composite, or compomer (Dyract) and three resin modified glass ionomer cements (Fuji II LC, Photac-Fil, and Vitremer) and to compare the use of 3 units for measuring fluoride ...three ...

101

Protection and Reinforcement of Tooth Structures by Dental Coating Materials

Protection and Reinforcement of Tooth Structures by Dental Coating Materials

... Monomer penetration into dentin and its polymerization in situ creates a hybrid layer, which is essential to obtain good bonding to dentin [3]. Theoretically, the hybrid layer can provide marginal sealing of the cavity ...

11

Flexural Strength of Temporary Restorative Materials Stored in Different Solutions

Flexural Strength of Temporary Restorative Materials Stored in Different Solutions

... methacrylate-based resin and three bis-acryl resin provisional materials using an in vitro model test ...late-based resin (Takilon) showed the least fracture strength ...bis-acryl resin ...

8

Esthetic smile rehabilitation of anterior teeth by treatment with biomimetic restorative materials: a case report

Esthetic smile rehabilitation of anterior teeth by treatment with biomimetic restorative materials: a case report

... The advances in dental materials in recent years have revolutionized the concepts applied to restorative dentistry, making it basically an adhesive dentistry. The development of resinous materials and adhesive systems ...

5

A Spectrophotometric Evaluation of Color Change in Dental Composites due to Various Beverages by Cielab Technique: An In Vitro Study

A Spectrophotometric Evaluation of Color Change in Dental Composites due to Various Beverages by Cielab Technique: An In Vitro Study

... As these are direct esthetic restorative material the success of this restoration depends largely on their colour stability and their finishing surface.Change of color and loss of shade-match with surrounding tooth ...

86

Microleakage of Nanofilled Composite Resin Restorative Material

Microleakage of Nanofilled Composite Resin Restorative Material

... hybrid composite in all groups, but the dif- ference was not ...of composite restorations at the occlusal margins than at the gingival margins placed below the cemento-enamel junction (CEJ) and the ...

6

Cavity Bases Revisited

<p>Cavity Bases Revisited</p>

... posterior resin composite restorations, bonded with a two-step etch and rinse or self-etching adhesive, at 1 year and concluded that the bene fi t of placing a RMGI liner beneath a posterior resin ...

8

Effect of four different conditioners on the shear bond strength of composite to glass ionomer: An In vitro study

Effect of four different conditioners on the shear bond strength of composite to glass ionomer: An In vitro study

... by resin composite or amalgam in areas of high stress. Resin modified GIC has proved to be a material with improved properties and aesthetics as compared to the conventional glass ...the resin ...

91

The Use of Micro-Computed Tomography for Evaluation of Internal Adaptation of Dental Restorative Materials in Primary Molars: An In-Vitro Study

The Use of Micro-Computed Tomography for Evaluation of Internal Adaptation of Dental Restorative Materials in Primary Molars: An In-Vitro Study

... function. Resin composite has good esthetic and capability of forming a bond to enamel and dentin, thus its application in the restorative field has been ...of resin composite will result in a ...

9

Mechanical Properties of Epoxy Resin – Fly Ash Composite

Mechanical Properties of Epoxy Resin – Fly Ash Composite

... Two wooden moulds of size 154 X 78 X 12 (mms) were used for casting of polymer matrix composite slabs. The moulds made of pressed wood. The mould comprises of two plates one top & other bottom & third ...

12